沙伯基礎(chǔ)創(chuàng)新PC LEXAN HF1110R 產(chǎn)品特性及用途：超高流動性，良好的脫模性，良好的成型性，用于鏡頭，光學(xué)數(shù)據(jù)存儲，安全設(shè)備，薄壁零件，鏡片等
我公司提供的產(chǎn)品均為正牌塑膠原料，品質(zhì)保證，貨源穩(wěn)定，送貨上門，可免費提供官方物性表、UL黃卡，并隨貨提供RoHS報告、SGS報告等，索取權(quán)威資料請致電13268582149
PC HF1110R 物性表：
| Physical | Nominal Value | Unit | Test Method |
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 25 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 to 0.70 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
| Tensile Strength 2 (Yield) | 62.1 | MPa | ASTM D638 |
| Tensile Strength 2 (Break) | 65.5 | MPa | ASTM D638 |
| Tensile Elongation 2 (Break) | 120 | % | ASTM D638 |
| Flexural Modulus 3 (50.0 mm Span) | 2310 | MPa | ASTM D790 |
| Flexural Strength 3 (Yield, 50.0 mm Span) | 93.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
| Notched Izod Impact (23°C) | 640 | J/m | ASTM D256 |
| Instrumented Dart Impact (23°C, Energy at Peak Load) | 54.2 | J | ASTM D3763 |
| Tensile Impact Strength 4 | 378 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 127 | °C | ASTM D648 |
| Flammability | Nominal Value | Unit | Test Method |
| Flame Rating - UL (1.09 mm) | V-2 | UL 94 | |
| UL | Nominal Value | Unit | Test Method |
| RTI Str | 130 | °C | UL 746 |
| RTI Imp | 130 | °C | UL 746 |
| RTI Elec | 130 | °C | UL 746 |