| 項(xiàng) 目 Property |
單 位 Unit |
試驗(yàn)方法 Test Method |
試驗(yàn)條件 Test Condition |
AG15A2 |
|
抗張強(qiáng)度 |
kg/cm2 ( MPa) |
ASTM D-638 ( ISO527) |
23℃ |
470 (46) |
| 彎曲強(qiáng)度 Flexural Strength |
kg/cm2 ( MPa) |
ASTM D-790 ( ISO178) |
23℃ |
840 (83) |
| 彎曲模數(shù) Flexural Modulus |
kg/cm2 |
ASTM D-790 ( ISO178) |
23℃ |
28000 (2750) |
| 洛式硬度 Rockwell Hardness |
R-Scale | ASTM D-785 ( ISO2039/2 ) |
23℃ |
R-108 |
| Izod衝擊強(qiáng)度 Izod Impact Strength |
kg-cm/cm ( J/m ) |
ASTM D-256 ( ISO R180 ) |
23℃ 1/4'' 厚 |
20 (196) |
| 衛(wèi)氏軟化點(diǎn) Vicat Softening Point |
℃ | ASTM D-1525 (ISO 306) |
1 Kg Load |
104 |
| 熱變形溫度 Heat Deflection Temperature |
℃ | ASTM D-648 (ISO 75/A) |
Unannealed 18.6kg/cm2 ( 1/2'' 厚 ) |
89 |
| Annealed 18.6kg/cm2 ( 80 ℃×8Hr) |
101 |
|||
| 熔融指數(shù) Melt Flow Index |
g/10 min | ASTM D-1238 ( ISO1133 ) |
200℃×5Kg ( 49N ) |
1.7 |
| 220℃×10Kg ( 98N ) |
19 |
|||
| 收縮率 Molding Shrinkage |
% | FCFC Method |
23℃ | 0.4~0.7 |
| 比 重 Specific Gravity |
ASTM D-792 ( ISO1183 ) |
23℃/23℃ |
1.05 |
|
| 燃燒性 Flammability |
UL-94 | FILE NO. E162823 |
1/16" HB All Color |